1、High closed pore rate
(1) polyether polyol: high proportion of ethylene oxide, high activity, more occurring in the replacement of polyether polyol with different activities;
(2) process formula: stannous octanoate dosage, high activity of isocyanate, large cross-linking, fast cross-linking speed, too much amine and physical blowing agent
The internal pressure of the foam is low, and the foam elasticity cannot be opened when the TDI index is too large, which will also lead to high closed-hole rate.
2、Shrinkage (gel speed is greater than the speed of foaming)
(1) High closed pore rate, shrinkage when cooling;
(2) process conditions: low temperature, low material temperature;
(3) process formula: excessive silicone oil, excessive physical foaming agent, TDI index is too low.
3、Inside crack
(1) Process conditions: low temperature, high temperature of reaction center;
(2) process formula: low TDI index, more tin, high early foaming strength;
(3) high activity of silicone oil, less dosage.
4, top crack (hair gas gel speed imbalance)
(1) process conditions: low temperature, low material temperature;
(2) process formula: catalyst dosage is not enough, amine dosage is less, silicone oil quality is not good.
5, the bottom corner of the crack (too much amine, foaming speed is too fast)
Surface macropore: excessive amount of physical foaming agent, silicone oil and catalyst quality is poor.
6、Poor low temperature performance of foam
Poor intrinsic quality of polyether polyol, in the same hydroxyl value, low functionality, unsaturation, the same amount of tin, TDI index is low.
7、Poor ventilation
(1) climatic conditions: low temperature
(2) raw materials: high polyether polyol, high silicone oil activity;
(3) process formula: more tin, or the same amount of tin when the water and amine content is less, TDI index is high.
8、Different inverse elasticity
(1) raw materials: high activity of polyether polyol, small relative molecular mass, high activity of silicone oil;
(2) process formula: large amount of silicone oil, more tin, more water in the same amount of tin, high TDI index.
9、Poor tensile strength
(1) raw materials: too many low-molecular polyether polyol, the same hydroxyl value of low functionality;
(2) process formula: less tin gel reaction is not good, in the same amount of tin, TDI index is high, less water cross-linking degree is low.
10、Smoke when foaming
Excess amine prompted by the reaction between water and TDI released a lot of heat, low boiling point material evaporation and smoke. If it is not scorched, the smoke is mostly from TDI, low boiling point substances and polyether polyethylene.
low boiling point substances and polyether polyol monomer naphthenic composition.
11、Foam with white rib
Foam and gel reaction speed, in the continuous foam transfer speed is slow, local extrusion and generate a dense layer, the phenomenon of white rib. Should
Timely increase the transfer speed, or reduce the material temperature, reduce the amount of catalyst.
12、Crispy foam
There is more water in the recipe, the generation of diurea has not been dissolved in silicone oil, poor tin catalyst, cross-linking reaction is not sufficient, small relative molecular mass of polyether polyol, the content of polyether polyol is high.
The content of polyether polyol is too much, the reaction temperature is too high, and the breaking of ether bond reduces the foam strength.
13、Foam density is lower than the set value
Foam index is too large because of inaccurate measurement, high temperature and low air pressure.
14、The foam has bottom skin, side skin, bottom step cavitation
Tin polyamine less, slow foaming speed, fast gel speed, in continuous foaming with temperature too low.
15、Large elongation rate
(1) raw materials: polyether polyol activity is high, functional degree is small;
(2) process formula: TDI index low crosslinking is not enough, more tin, more silicone oil;